OM1, 62.5 µm MM, 500 µm Coated

This item cannot be purchased online. Contact Customer Service to purchase this item.
  • Item #500 µm Coated Graded Index Multimode Fibers, 62.5/125
Item Number
500 µm Coated Graded Index Multimode Fibers, 62.5/125

Description
OM1, 62.5 µm MM, 500 µm Coated


Applications
Aerospace, Geophysical, Industrial, Military, Transportation


Numerical Aperture0.275 ± 0.015
Core Diameter62.5 ± 2.5 (µm)
Operating Temperature Range-40 to +85 (ºC)
Coating Diameter500 ± 25 (µm)
Clad Non-Circularity≤ 1 (%)
Core Non-Circularity≤ 5 (%)
Coating Non-Circularity≤ 5 (%)
Clad Diameter125 ± 1 (µm)
Single-Mode or MultimodeMultimode
Performance CharacteristicOM1
Core/Clad Concentricity Error (Offset)≤ 1.0 (µm)
Tensile Proof Test100 (kpsi)
Tensile Proof Test0.69 (GPa)
Typical Coating Strip Force0.6 (lbf)
Typical Coating Strip Force2.7 (N)
Attenuation at 850 nm≤ 2.9 (dB/km)
Attenuation at 1300 nm≤ 0.6 (dB/km)
Standard Bandwidth at 850 nm≥ 200 (MHz-km)
Standard Bandwidth at 1300 nm≥ 500 (MHz-km)
Laser-Optimized Bandwidth at 850 nm≥ 220 (MHz-km)
Laser-Optimized Bandwidth at 1300 nm≥ 500 (MHz-km)
Attenuation at 1380 nm minus attenuation at 1300 nm≤ 1.0 (dB/km)
Attenuation Uniformity/Point Discontinuities at 850 and 1300 nm ≤ 0.08 (dB)
Zero Chromatic Dispersion Wavelength (λ0)1320 to 1365 (nm)
Zero Chromatic Dispersion Slope (S0)≤ 0.001 x (1458 – λ0), ≤ 0.11 ps/nm2-km, (1320 ≤ λ0 ≤ 1348 nm), (1348 ≤ λ0 ≤ 1365 nm) (ps/(nm²·km))
Group Refractive Index at 850 nm1.496
Group Refractive Index at 1300 nm1.491
Backscatter Coefficient at 850 nm-68.4 (dB)
Backscatter Coefficient at 1300 nm-72.1 (dB)
Macrobend Attenuation 100 Turns on a 75 mm Mandrel at 850 nm and 1300 nm≤ 0.5 (dB)
Temperature Induced Attenuation at 850 and 1300 nm from -60 to +85 ºC (5 24-Hour Cycles) ≤ 0.2 (dB/km)
Accelerated Aging (Temperature) Induced Attenuation at 85 ºC for 30 days≤ 0.2 (dB/km)
Water Immersion Induced Attenuation, 23 ºC for 30 Days≤ 0.2 (dB/km)
Dynamic Fatigue Stress Corrosion Parameter (nd) ≥ 18
Standard Reel Lengths1.1 to 4.4 (km)
Coating-Clad Concentricity Error (Offset)≤ 19 (µm)
Coating Strip Force Range0.2 – 1.0 lbf, 0.9 - 4.4 N