The high-numerical aperture low-OH content of these UltraSil® Optical Fibers result in a large usage window. Low OH concentration is especially effective for using these fibers in near-IR spectroscopy applications.

For laser delivery, HCS® fiber coating preserves cladding modes through bends and distributes lost power over a greater area—lowering the probability of “hot spots.” PYRO options use PYROCOAT® coating only.

For high-temperature performance, we recommend PYROCOAT® polyimide coating. This coating also strips cladding modes for enhanced performance in sensing and spectroscopy applications.
Unit of Measure

Optical Properties

Type

N/A Multimode Step-Index

Numerical Aperture

N/A 0.29

Attenuation

N/A @ 850 nm, ≤ 12 dB/km

Water Content

N/A Low OH

Dimensions/Geometric Properties

Core Diameter

N/A 200 ± 6 µm

Cladding Diameter

N/A 240 ± 5 µm

Coating Diameter

N/A 270 ± 5 µm

Buffer Diameter

N/A unbuffered

Coating Concentricity

N/A ≥ 80%

Crimp & Cleave Compatible

N/A No

Coating/Buffer Descriptions

Coating Material

N/A PYROCOAT®

Operating Temperature

N/A -65 to +300 ºC

Mechanical and Testing Data

Short-Term Bend Radius

N/A ≥ 18 mm

Long-Term Bend Radius

N/A ≥ 30 mm

Proof Test Level

N/A ≥ 100 kpsi0.689 GPa

How To Order:

Product Description Code

N/A TCE-HB200H

Order From Location

N/A AVON LOCATION
1.888.438.9936 toll-free in the United States and Canada
1.860.678.0371 from outside the U.S.A.
55 Darling Drive
Avon, CT 06001, USA

Order By Item #

N/A BF04830-01

Note

N/A OFS polyimide optical fibers are known to operate in environments up to 300 °C. Performance is application dependent. Contact our Technical Sales department to discuss your specific application requirements. 1-860-678-6636

Typical Applications

N/A FTIR Spectroscopy General Fiber-Optic Sensing High-Temperature Process Control Near-IR Spectroscopy Raman Spectroscopy Remote High Temperature Sensing

Options

N/A Clad Diameter Connectorization Core Diameter Metalization Numerical Aperture Proof Test