The high-numerical aperture low-OH content of these UltraSil® Optical Fibers result in a large usage window. Low OH concentration is especially effective for using these fibers in near-IR spectroscopy applications.
For laser delivery, HCS® fiber coating preserves cladding modes through bends and distributes lost power over a greater area—lowering the probability of “hot spots.” PYRO options use PYROCOAT® coating only.
For high-temperature performance, we recommend PYROCOAT® polyimide coating. This coating also strips cladding modes for enhanced performance in sensing and spectroscopy applications.
For laser delivery, HCS® fiber coating preserves cladding modes through bends and distributes lost power over a greater area—lowering the probability of “hot spots.” PYRO options use PYROCOAT® coating only.
For high-temperature performance, we recommend PYROCOAT® polyimide coating. This coating also strips cladding modes for enhanced performance in sensing and spectroscopy applications.
Item # |
Item Name |
Attenuation |
Core Diameter |
Cladding Diameter |
Coating Diameter |
Buffer Diameter |
Coating Material |
Buffer Material |
---|---|---|---|---|---|---|---|---|
![]() | ||||||||
BF04746-01 | N/A 200 0.29 NA Optical Fiber | N/A @ 850 nm, ≤ 12 dB/km | N/A 200 ± 6 µm | N/A 240 ± 5 µm | N/A 260 +5/-10 µm | N/A 375 ± 30 µm | N/A HCS® | N/A ETFE |
BF04830-01 | N/A 200 PYRO 0.29 NA Optical Fiber | N/A @ 850 nm, ≤ 12 dB/km | N/A 200 ± 6 µm | N/A 240 ± 5 µm | N/A 270 ± 5 µm | N/A unbuffered | N/A PYROCOAT® | N/A |
BF05246 | N/A 272 Blue 0.29 NA Optical Fiber | N/A @ 850 nm, ≤ 12 dB/km | N/A 272 ± 10 µm | N/A 326 ± 10 µm | N/A 356 ± 10 µm | N/A 420 ± 30 µm | N/A HCS® | N/A ETFE (Blue) |
BF04830-02 | N/A 320 PYRO 0.29 NA Optical Fiber | N/A @ 850 nm, ≤ 12 dB/km | N/A 320 ± 10 µm | N/A 385 ± 8 µm | N/A 415 ± 5 µm | N/A unbuffered | N/A PYROCOAT® | N/A |
BF04746-02 | N/A 330 0.29 NA Optical Fiber | N/A @ 850 nm, ≤ 12 dB/km | N/A 330 ± 10 µm | N/A 400 ± 8 µm | N/A 430 +5/-10 µm | N/A 730 ± 30 µm | N/A HCS® | N/A ETFE |